Heat-treated glass forms when annealed architectural glass is heated to around 1,150°F in a tempering oven. We then rapidly cool both sides using high-pressure air, a process known as quenching. This creates permanent surface compression zones. As a result, the glass gains higher compressive strength and greater resistance to impact and thermal stress. There are […]